Active TopicsActive Topics  Display List of Forum MembersMemberlist  CalendarCalendar  Search The ForumSearch  HelpHelp
  RegisterRegister  LoginLogin  Old ForumOld Forum  Twitter  Facebook

Science & Technology
 IslamiCity Forum - Islamic Discussion Forum : General : Science & Technology
Message Icon Topic: Sharpest cut from nanotube sword Post Reply Post New Topic
Author Message
Male  Islam
Senior Member
Senior Member
Senior Member

Joined: 01 March 2000
Online Status: Offline
Posts: 2550
Quote rami Replybullet Topic: Sharpest cut from nanotube sword
    Posted: 17 September 2007 at 8:33am
Bi ismillahi rahmani raheem

assalamu alaikum

Sharpest cut from nanotube sword

Carbon nanotech may have given swords of Damascus their edge.

Katharine Sanderson

Damascus sabres may get their pattern and strength from nanotubes in the steel.

Alexander Dietsch
Think carbon nanotubes are new-fangled? Think again. The Crusaders felt the might of the tube when they fought against the Muslims and their distinctive, patterned Damascus blades.

Sabres from Damascus, now in Syria, date back as far as 900 AD. Strong and sharp, they are made from a type of steel called wootz.

Their blades bear a banded pattern thought to have been created as the sword was annealed and forged. But the secret of the swords' manufacture was lost in the eighteenth century.

Materials researcher Peter Paufler and his colleagues at Dresden University, Germany, have taken electron-microscope pictures of the swords and found that wootz has a microstructure of nano-metre-sized tubes, just like carbon nanotubes used in modern technologies for their lightweight strength.

The tubes were only revealed after a piece of sword was dissolved in hydrochloric acid to remove another microstructure in the swords: nanowires of the mineral cementite.

Wootz's ingredients include iron ores from India that contain transition-metal impurities. It was thought that these impurities helped cementite wires to form, but it wasn't clear how. Paufler thinks carbon nanotubes could be the missing piece of the puzzle.

At high temperatures, the impurities in the Indian ores could have catalysed the growth of nanotubes from carbon in the burning wood and leaves used to make the wootz, Paufler suggests. These tubes could then have filled with cementite to produce the wires in the patterned blades, he says.

But his suggestion isn't necessarily rock solid. Steel expert John Verhoeven, of Iowa State University in Ames, suggests Paufler is seeing something else. Cementite can itself exist as rods, he notes, so there might not be any carbon nanotubes in the rod-like structure.

Another potential problem is that TEM equipment sometimes contains nanotubes, says physicist Alex Zettl of the University of California, Berkeley. Paufler admits it is difficult to exclude the problem but says that, having studied the swords with a range of different equipment, he is convinced that the tubes he sees are from the swords.

If Paufler is right, nanotube researchers do not mind being pre-empted by Indian steel-makers. "The important fact is that nanotubes were serving some very useful purpose even before they were discovered," says chemist Andrei Khlobystov of the University of Nottingham, UK. "This should inspire us to look for new practical applications of these remarkable nanostructures."

The next step, says Paufler, will be to take the latest carbon nanotube knowledge and work with bladesmiths to try and recreate the lost process.

Edited by rami
Rasul Allah (sallah llahu alaihi wa sallam) said: "Whoever knows himself, knows his Lord" and whoever knows his Lord has been given His gnosis and nearness.
IP IP Logged
Male  Islam
Senior Member
Senior Member
Senior Member

Joined: 01 March 2000
Online Status: Offline
Posts: 2550
Quote rami Replybullet Posted: 17 September 2007 at 8:45am
Bi ismillahi rahmani raheem

Damascus steel

From Wikipedia, the free encyclopedia

• •

Damascus steel is a steel used in Middle Eastern swordmaking from about 1100 to 1700AD. Damascus swords were of legendary sharpness and strength, and were apocryphally claimed to be able to cut through lesser quality European swords and even rock. The exact technique used to create original Damascus steel is now a matter of historical conjecture.

Damascus swords often had an obvious patterned texture on their surface. Several other steelmaking techniques also result in patterned surfaces, and have often been sold as Damascus steel, Damascened steel and sometimes watered steel. The most common technique for producing these materials is the pattern welding, which is today widely used for custom knife making. Skilled swordsmiths can manipulate the patterns to mimic the complex designs found in the surface of the original, medieval Damascus steel.

Another theory behind the hardness of Damascus steel is that the steel contains a small amount of vanadium, which would theoretically strengthen the blade.


Origin of the term Damascus

The origins of the name Damascus remains somewhat controversial. Although it would seem obvious that it refers to swords forged in Damascus, there are several equally likely sources of the name. One potential source is the swordsmith himself: the author al-Beruni refers to swords made by a man he names Damasqui. Another author, al-Kindi, refers to swords made in Damascus as Damascene. This word has often been employed as an epithet in various Eastern European legends (Sabya Damaskinya or Sablja Dimiskija meaning "Damascene sword"), of which perhaps the best known are the Serbian legends of Prince Marko, an historical figure of the late 14th Century in what is now the Republic of Macedonia.


The original Damascus steel swords may have been made in the vicinity of Damascus, Syria, in the period from 900AD to as late as 1750AD. Damascus steel is a type of steel alloy that is both hard and flexible, a combination that made it ideal for the building of swords. It is said that when Damascus-made swords were first encountered by Europeans during the Crusades, it garnered an almost mythical reputation—a Damascus steel blade was said to be able to cut a piece of silk in half as it fell to the ground, as well as being able to chop through normal blades, or even rock, without losing its sharp edge. Recent metallurgical experiments, based on microscopic studies of preserved Damascus-steel blades, have claimed to reproduce a very similar steel via possible reconstructions of the historical process[citation needed].

When forming a batch of steel, impurities are added to control the properties of the resulting alloy. In general, notably during the era of Damascus steel, one could produce an alloy that was hard and brittle at one extreme by adding up to 2% carbon, or soft and malleable at the other, with about 0.5% carbon. The problem for a swordsmith is that the best steel should be both hard and malleable — hard, so as to hold an edge once sharpened, but malleable so it would not break when hitting other metal in combat. This was not possible with normal processes.

Metalsmiths in India and Sri Lanka perhaps as early as 100BC developed a new technique known as wootz steel that produced a high-carbon steel of unusually high purity. Glass was added to a mixture of iron and charcoal and then heated. The glass would act as a flux and bind to other impurities in the mixture, allowing them to rise to the surface and leave a more pure steel when the mixture cooled. Thousands of steel making sites were found in Samanalawewa area in Sri Lanka that made high carbon steel as early as 300BC. (Juleff, 1996). These steel making furnaces were built facing western monsoon winds and wind turbulence and suction was used to create heat in the furnace. Steel making sites in Sri Lanka have been dated to 300BC using carbon dating technology. The technique propagated very slowly through the world, reaching modern-day Turkmenistan and Uzbekistan around 900AD, and then the Middle East circa 1000AD.

This process was further refined in the Middle East, either using locally produced steels, or by re-working wootz purchased from India. The exact process remains unknown, but allowed carbides to precipitate out as micro particles arranged in sheets or bands within the body of a blade. The carbides are far harder than the surrounding low carbon steel, allowing the swordsmith to make an edge which would cut hard materials with the precipitated carbides, while the bands of softer steel allowed the sword as a whole to remain tough and flexible.

The banded carbide precipitates appear in the blade as a swirling pattern. By manipulating the ingot of steel in a certain way during forging, various intentional patterns could be induced in the steel. The most common of these was a pattern of lateral bands, often called 'Muhammed's Ladder', most likely formed by cutting or forging notches into the surface of the ingot, then forging it into the blade shape (this is the method Pendray (below) used to reproduce the pattern). The notches resulted in different degrees of work hardening between top and bottom, and thus controlled the size of the carbide particles in the surface at those areas, and thus the appearance of the bands.

A team of researchers based at the Technical University of Dresden that uses x-rays and electron microscopy to examine Damascus steel discovered the presence of cementite nanowires[1] and carbon nanotubes.[2] Peter Paufler, a member of the Dresden team, says that these nanostructures give Damascus steel its distinctive properties[3] and are a result of the forging process.[4] However, metallurgist John Verhoeven of Iowa State University, who also specializes in the study of Damascus steel, dismisses the importance of the nanostructures, which he believes are naturally occurring and would be found in normal steel.[5] However, there is no information available to support his claim.

Loss of the technique

For reasons that are not entirely clear, but possibly because sources of ores containing trace amounts of tungsten and/or vanadium needed for its production were depleted, the process was lost to the middle-eastern metalsmiths circa 1750AD. It has been eagerly sought by many since that time.

It has long been argued that the raw material for Damascus steel swords was imported from India, because India was the only known center of crucible-fired steels like wootz. However this conclusion became suspect when the furnaces in Turkmenistan were discovered, demonstrating at least that the technique was moving out from India. The wootz may have been manufactured locally in the Damascus area, but so far no remains of the distinctive wootz furnaces have appeared. The work of Verhoeven et al. supports the hypothesis that the wootz used was from India, as several key impurities that appear to give Damascus steel its properties point to particular ores available only in India.

The Russian bulat steel has many similar properties, at least in nature if not in process. Recently various groups have claimed to have recreated steel with properties consistent with true Damascus blades, through experimental archaeology, though even they admit they cannot be certain how it was originally created. Verhoeven et al. (1998) argued that the keys are ores with certain trace elements, controlled thermal cycling after the initial forging, and a grinding process to reveal the final damask pattern. A somewhat different technique was proposed by Wadsworth and Sherby (1980; also 2001).

The recent discovery of carbon nanotubes in the steel's composition has also brought to light a new hypothesis which might explain the loss of the technique. Carbon nanotubes (perhaps the strongest and stiffest material known), while occurring randomly in nature (simple campfires produce some nanotubes), require fairly high-tech, high-energy production methods to be made useful as structural materials. Therefore, ancient smiths, with the level of technology at their disposal, could hardly control the formation of these nanometer-scale carbon structures. Some element of random chance (forging, alloy composition, heat treatment, smelting process, environmental particularities, etc.) might have been responsible for the formation of these structures, which could not only explain some of their "legendary" qualities, but also the reason why, to this day, these properties have never been successfully emulated.

Attempts at reproduction

From the very start, the superior capabilities of Damascus swords attracted significant attention, and many attempts were made to reproduce either the performance or the appearance of the Damascus blades. Since pattern welding was a widespread technique, and produced surface patterns similar to those found on Damascus blades, many people believed that Damascus blades were made using a pattern welding technique. This belief was challenged in the 1990s when J. D. Verhoeven and A. H. Pendray published an article on their experiments on reproducing the elemental, structural, and visual characteristics of Damascus steel.

Verhoeven and Pendray started with a cake of steel that matched the properties of the original wootz steel from India, which also matched a number of original Damascus swords they had access to. The wootz was in a soft, annealed state, with a large grain structure, and many beads of pure iron carbide which were the result of the hypereutectoid state of the wootz. They had already determined that the grains on the surface of the steel were grains of iron carbide, so their question was how to reproduce the fine iron carbide patterns they saw in the Damascus blades from the large grains in the wootz.

By heating the cake of wootz to just below the critical temperature which would cause the iron carbide to return to solution, it was possible to forge the wootz with hand tools. Repeated forging, working the wootz into a long, thin shape suitable for a knife or sword blade, caused the large iron carbide crystals to fracture and spread out in the pearlite matrix. The resulting steel contains bands of iron carbide in a pearlite matrix, alternating with bands of ferrite and cementite. In this process the steel work hardens, which is what allows the normally soft wootz to be used for knives and swords.

Pattern welded "Damascened" steel

Pattern welded "Damascened steel" pocket knife
Pattern welded "Damascened steel" pocket knife
Main article: Pattern welding

It used to be believed that Damascus steel was made using pattern welding because the layering revealed by etching a pattern-welded blade in acid is similar to that of Damascus steel.

Pattern welded steel is commonly sold today as "Damascus steel", though it appears that the original Damascus steel was not created with that technique. Pattern welded Damascus is made out of several types of steel and iron slices, which are then welded together to form a billet. The patterns vary depending on what the smith does to the billet. The billet is drawn out and folded until the desired number of layers are formed. The end result, if done well, bears a strong resemblance to the surface appearance of a true Damascus blade, though the internal structure is completely dissimilar.

Another material similar to pattern weld is mokume-gane. Mokume is made of the softer metals, like gold, silver, and copper. It is made in much the same way as pattern weld Damascus, and is used for rings, tsubas (the guard on a katana), and knife bolsters. The name mokume-gane means "wood eye", referring to the pattern of the metals, which looks like wood grain. It was first made by the Japanese.

Some old shotgun barrels (usually on double barreled guns) were formed from wires that were wrapped around a mandrel and forged and welded into shape. This leaves a visible wire pattern, similar to a fingerprint in the barrel and such are referred to as "Damascus Barrels". Guns made with Damascus barrels are significantly weaker than fluid steel barrels, and more prone to corrosion and failure due to the welds along the length of the barrels. Damascus barrel shotguns should be examined by a qualified gunsmith and proof tested before use, to ensure that the barrels are sound before using the shotgun. The use of modern nitro cordite shotgun cartridges in an antique damascus barreled shotgun would cause the barrel to fail with dangerous consequences. Damascus barrels are only proofed for the use of traditional black powder which has much less ballistic energy than cordite. Damascus was used to manufacture shotgun barrels as choke boring was not mastered. It was far simpler to forge and weld the damascus around a mandrel to achieve the choke than it was to bore a fluid steel barrel. Choke boring was finally perfected by W.W. Greener near the end of the nineteenth century.

See also


  1. ^ Kochmann, W.; Reibold M., Goldberg R., Hauffe W., Levin A. A., Meyer D. C., Stephan T., Müller H., Belger A., Paufler P. (2004). "Nanowires in ancient Damascus steel". Journal of Alloys and Compounds 372: L15–L19. ISSN 0925-8388. 
    Levin, A. A.; Meyer D. C., Reibold M., Kochmann W., Pätzke N., Paufler P. (2005). "Microstructure of a genuine Damascus sabre". Crystal Research and Technology 40 (9): 905–916. DOI:10.1002/crat.200410456. 
  2. ^ Reibold, M.; Levin A. A., Kochmann W., Pätzke N., Meyer D. C. (16). "Materials:Carbon nanotubes in an ancient Damascus sabre". Nature 444: 286. DOI:10.1038/444286a. 
  3. ^ ech-swords.html
  4. ^ Sanderson, Katharine. "Sharpest cut from nanotube sword: Carbon nanotech may have given swords of Damascus their edge", Nature (journal), 2006-11-15. Retrieved on 2006-11-17. 
  5. ^ ech-swords.html


  • G. Juleff, "An ancient wind powered iron smelting technology in Sri Lanka", Nature 379 (3), 60-63 (January, 1996)
  • Eric M. Taleff, Bruce L. Bramfitt, Chol K. Syn, Donald R. Lesuer, Jeffrey Wadsworth, and Oleg D. Sherby, "Processing, structure, and properties of a rolled ultrahigh-carbon steel plate exhibiting a damask pattern," Materials Characterization 46 (1), 11-18 (2001).
  • J. D. Verhoeven, "A review of microsegregation induced banding phenomena in steels", J. Materials Engineering and Performance 9 (3), 286-296 (2000).
  • J. D. Verhoeven, A. H. Pendray, and W. E. Dauksch, "The Key Role of Impurities in Ancient Damascus Steel Blades", JOM 50 (9), 58-64 (1998).
  • J. Wadsworth and O. D. Sherby, "On the Bulat — Damascus steel revisited," Prog. Materials Science 68, 25-35 (1980).
  • Kochmann, W.; Reibold M., Goldberg R., Hauffe W., Levin A. A., Meyer D. C., Stephan T., Müller H., Belger A., Paufler P. (2004). "Nanowires in ancient Damascus steel". Journal of Alloys and Compounds 372: L15–L19. ISSN 0925-8388. 
  • Levin, A. A.; Meyer D. C., Reibold M., Kochmann W., Pätzke N., Paufler P. (2005). "Microstructure of a genuine Damascus sabre". Crystal Research and Technology 40 (9): 905–916. DOI:10.1002/crat.200410456. 
  • Reibold, M.; Levin A. A., Kochmann W., Pätzke N., Meyer D. C. (16). "Materials:Carbon nanotubes in an ancient Damascus sabre". Nature 444: 286. DOI:10.1038/444286a. 

External links

Edited by rami
Rasul Allah (sallah llahu alaihi wa sallam) said: "Whoever knows himself, knows his Lord" and whoever knows his Lord has been given His gnosis and nearness.
IP IP Logged
Post Reply Post New Topic
Printable version Printable version

Forum Jump
You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot delete your posts in this forum
You cannot edit your posts in this forum
You cannot create polls in this forum
You cannot vote in polls in this forum

The opinions expressed herein contain positions and viewpoints that are not necessarily those of IslamiCity. This forum is offered to stimulate dialogue and discussion in our continuing mission of being an educational organization.
If there is any issue with any of the postings please email to icforum at or if you are a forum's member you can use the report button.

Note: The 99 names of Allah avatars are courtesy of


Sponsored by:
Islamicity Membership Program:
IslamiCity Donation Program
IslamiCity Arabic eLearning
Complete Domain & Hosting Solutions
Home for Muslim Tunes
Islamic Video Collections
IslamiCity Marriage Site